Sheet for dental alignment, made with a special mixture, transparent and elastic, that allows to realize a dental aligner that produces a delicate strength and therefore more constant. This specificity ...
Size: 12 mm - 30 mm
Flexural strength: 700 MPa - 1,200 MPa
... transition layers) is a dental multilayer zirconium oxide (4Y-TZP cervical, 5Y-TZP incisal) with natural color and translucency gradient and high flexural strength (1200 MPa cervical, 700 MPa incisal) for anterior- or ...
Hunan Vsmile Biotechnology Co. Ltd
Size: 10 mm - 25 mm
Flexural strength: 700 MPa - 1,050 MPa
... CAD CAM dental ceramic block dental material for Lab Transmittance:43%~57% Hardness:1250HV Colors:3D Multilayer Indication:Crown, Inlay, Onlay, Anterior, Implant Usage:denture ...
Shenzhen Yurucheng Dental Materials Co., Ltd.
... for implant planning[P Characteristics Contains X- ray visible powder. Homogeneous mix ensures best visibility. Prevents light scattering. Diameter: 95 - 100 mm. Thickness: 12, 14, 15, 16, 18, 20, 25 mm. Indications allows ...
Size: 12 mm - 25 mm
Flexural strength: 1,200 MPa
... gingival parts. Simplicity of use Orodent zirconia is pre-sintered at a low temperature in order to provide an easy-to-process material that wears tools down to a minimum, thus extending tools’ life. Natural Aesthetics Its ...
Orodent srl
... (20 min) heat-cure denture base acrylic designed for the manufacture of full or partial dentures. Can be processed using either long or short curing techniques in boiling water. Available in Dark pink. Standard pink ...
KEMDENT ASSOCIATED DENTAL PRODUCTS LTD
At Last, an Outstanding Universal Cement that Closes the Gap Against Microleakage! Predicta® Bioactive Cement provides exceptional bond strengths to all substrates including zirconia. It also offers next level bioactive performance ...
Parkell Inc.