Alloy dental material Elektra®

casting

Inlays Onlays, ¾ crowns, crowns Telescope crowns, conus crowns Bridges Wide-span bridges Cast posts / cores, bars, attachments Implant-supported superstructures Partial dentures Technical Data Composition (%): - Ag 58.3 | Pd 25.0 | Cu 14.7 | In 2.0 | Ru <1.0, Re <1.0, Li <1.0 ISO - 22674:2016 ADA Type - Noble Type / Color - 4 / White Density (g/cm³) - 10.4 Melting Range (Solidus/Liquidus): - 900 - 990 °C Elastic Modulus (GPa): - 105 - As Cast Softened Hardened Vickers Hardness: - 190 150 240 Tensile Strength (MPa): - 560 495 740 0.2% Proof Stress (MPa): - 475 340 740 Elongation (%): - 18 18 5 Advantages High strength Economical due to low density Excellent processing properties Wide range of indications Tested biocompatibility