Cobalt-chromium dental material

CAD/CAMmilling

Unique on the market with 255 Vickers hardness Greater precision Lower milling tool consumption Less strain on the machine spindle Composition in % Cobalt (Co) 66 % Chrome (Cr) 27 % Molybdenum (Mo) 6% Others Si, Mn Physical and mechanical features Solidus-liquidus temperature - 1307 ÷ 1417 °C Thermal expansion coefficient - (25 ÷ 500 °C) 14,3 x 10-6 K-1 – (25 ÷ 600 °C) 14,5 x 10-6 K-1 Melting point - 1470 °C Density - 8,4 g/cmc Vickers hardness - 255 HV10 Percentage elongation at fracture - 11 % Yield load strength - (Rp0.2) 395 MPa Modulus of elasticity - 233 GPa Maximium cooking temperature - 980°C Colour - White CE 0425 ACCORDING TO: ISO 9693, ISO 22674 Dimensions DISC CUT Ø98.5x15mm | DISC CUT Ø98.5×13.5mm | DISC CUT Ø98.5x16mm | DISC PLAIN Ø98.5x10mm | DISC CUT Ø98.5x12mm | DISC CUT Ø98.5x14mm | DISC CUT Ø98.5x18mm | DISC PLAIN Ø98.5x8mm | DISC CUT Ø98.5x20mm | DISC CUT Ø98.5x22mm | DISC CUT Ø98.5x25mm | DISC CUT Ø98.5x24mm | DISC CUT Ø98.5×24.5mm