Alloy dental material MoguCera C Disc

CoCrMofor dental bridgesfor dental crowns

CoCrMo milling disc with excellent properties for the manufacture of crowns, bridges, frameworks, telescopes, bars, attachments and implant supported superstructures. MoguCera C Disc is based on a non-precious ceramic alloy already used in the conventional casting technology. Free of nickel, beryllium, lead und cadmium. Type 4 pursuant to DIN EN ISO 22674 with a very wide range of indications. Advantages for users: Medium hardness of 288 HV 10 Excellent metal-ceramic Bonding Easy to work with and very to polish Laser weldable Suitable for dry and wet milling Composition in percent by mass: Co - 65% Cr - 28% Mo - 5% C,Si,Nb,Mn,Fe - <1% Technical properties: Proof stress (Rp 0.2) - 413MPa Ultimate tensile strength - 597MPa Elongation - 12% Elastic modulus - 206GPa Vickers hardness - 288HV10 Density - 8.3g/cm³ CTE (20-500°C) - 14.5 x 10⁻⁶K⁻¹ CTE (20-600°C) - 14.8 x 10⁻⁶K⁻¹ Laser weldable - Yes Type (DIN EN ISO 22674) - 4