Zfx biocompatible dental materials

Size: 98 mm
Flexural strength: 1,300 MPa - 1,450 MPa

The blanks impress with their strength and their hydrothermal long-term resistance. A completely homogeneous joint is produced by using a specially developed manufacturing process. The balanced composition and fine grain structure ...

Size: 98 mm
Flexural strength: 1,250 MPa

... translucency and strength for the production of highly aesthetic fully-monolithic restorations. Because of a newly-developed material composition (4Y-TZP) and optimized manufacturing processes, a hybrid micro-joint is ...

Size: 98 mm
Flexural strength: 750 MPa

... oxide, therefore setting new material standards. The cubic-tetragonal mixed microstructure produces a previously unachieved combination of light transmission and excellent technical properties. The result is a bio-compatible ...

Size: 98 mm
Flexural strength: 1,100 MPa - 1,250 MPa

... combines the material properties of the „white“ Zfx Zirconium Color with a significant increase in light permeability. The material impresses with its cost-effectiveness, and also has all of the advantages ...

Size: 98 mm
Flexural strength: 1,250 MPa

Based on the „Zfx Cubic – high strength cubic zirconia system“, the Cubic ML blanks provide a flowing color graduation from cervical to incisal. The production of aesthetic monoliths is more efficient than ever before.

Size: 98 mm
Flexural strength: 750 Pa - 800 Pa

... zirconium oxide that sets new material standards. Due to the cubic-tetragonal mixed microstructure, a light transmission thathas not been achieved up to now, is combinded with excellent mechanical properties. The result ...

Size: 98 mm

The Zfx Poly X ML blanks consist of methyl methacrylate (PMMA)-based multi-layer acrylic polymer, with toxic or allergenic substances (in accordance with ISO 10993-5).

Size: 98 mm

The Zfx PMMA Temp blanks consist of thermoplastic acylic polymer based on Methyl methacrylate (PMMA),without toxic or allergenic substances.